Ni-P-Sn layers were deposited on the steel strip, with less carbon, by electroless method. An electrolyte based on nickel chloride, sodium hypophosphite, tin chloride and additions for bath optimizing were utilized. The influence on the deposited layers characteristics of different amounts of tin chloride in the nickel bath, respectively, 0.1g/L and 0.4g/L was studied. The conditions for electrolyte formation and optimum working parameters: pH and temperature were set. Ni-P-Sn layers were characterized by comparis...

The research consisted in obtaining Ni-P and Ni-P-Al2O3 coatings followed by heat treatment and characterization of heat treated and untreated layers. The layers were deposited on the steel strip, by electroless method to certain process parameters. To obtain the Ni-P-Al2O3 nanocomposite layers, 5 g/L Al2O3 particles of 20 nm were introduced into the nickel bath, and it has been worked with the same parameters as to obtain the Ni-P layer. The samples were heat treated at 300 0C, 400 0C and 5000C for one hour in a ...