The aim of this work is the optimization of sinter-crystallization regime of a glassceramic from a municipal solid waste incineratior (MSWI) bottom ash. The parent waste was melted at 1400oC, milled below 75 $\mu$m and the obtained glass powders were pressed at 100 MPa. The optimal temperature for sinter-crystallization was estimated by DTA, dilatometry and XRD. Subsequently, the degrees of sintering, obtained at different heating rates (between 2 and 40oC/min) and 1 h step at 950oC were estimated by the linear sh...

The possibility to obtain a low cost petrurgical material by direct sintering of alkaline basaltic tuffs is demonstrated. The parent rock was milled for 10-15 min and the resulting powder was pressed at 100 MPa. The sintering and the phase formation in air and inert atmospheres were studied by dilatometry and DTA, respectively. The phase composition of obtained samples was evaluated by XRD whereas the stricture was highlighted in details by SEM. Some mechanical and thermal properties of the new materials were meas...

This paper presents the results obtained by utilization of pulverized coal fly ash both as raw mix component for Portland cement clinker and as admixture to cement type CEM II/B-V, too. The fly ash was analyzed from point of view of chemical, mineralogical and of radioactivity content. Two samples of raw mixes were prepared, one with raw materials as a reference sample consisting from limestone, clay, sand and pyrite cinder, and another with 10.14\% fly ash instead of clay. Raw mixes were ground at a fineness expr...

The production of the agglomerate is always related to the consumption of energy, occurrence of solid polluting substances and emissions, which are the main source of air pollution. The submitted work contains the analysis of knowledge obtained from the literature, but mainly analysis of the results gained from the laboratory sintering pan. This laboratory sintering pan sufficiently simulates conditions present on the sinter belt in relation to the production of CO, CO2, NOx, SOx and solid polluting substances in ...

The possibility to obtain new eco-compatible building materials by milling, pressing and direct sintering of secondary raw materials (SRM) derived from a physical/mechanical treatment of municipal solid waste incinerator (MSWI) bottom ashes is discussed. The chemical compositions and particle size distribution of used SRM press powders were evaluated using XRF analysis and by laser granulometer, respectively. The thermal and densification behaviours were studied by non-isothermal DTA-TG and dilatometric techniques...