An electrolyte for chromium based nano-composite electrolytic coatings (nano-CE?) obtaining has been developed. Nano-CEC was applied on steel of the St 3 brand with constant exposure to ultrasound, electrolyte temperature 50?60°?, current density 7kA/m2 for 1 and 2 hours from two variants of chromium-plating electrolytes, differing in the fact that one electrolyte contained strontium sulfate, in the other ? without it. Quantitative assessment of the corrosion resistance of nano - CEC deposited on steel St.3, was e...

The influence of ?-ferrite amount ferrite in AISI 321 steel on its general corrosion, critical pitting temperature and potential in simulated circulating waters. The samples were made in the form of rectangular 3x3x1 mm parallelepipeds by cold mechanical method. Surface of the samples was subjected to electro-polishing. The amount of ferrite phase was determined by empirical formula. It was established, that after electromagnetic saturation of the samples, ?-ferrite content in five heats of AISI 321 steel was calc...