Title: POSSIBILITIES OF AUSTEMPERED DUCTILE IRON (ADI) PRODUCTION
POSSIBILITIES OF AUSTEMPERED DUCTILE IRON (ADI) PRODUCTION

PlumX Article Metrics by Elsevier
Peter Futas; Alena Pribulova; Marcela Pokusova; Andrea Junakova; Vladimir Sabik
10.5593/sgem2022/1.1/s04.056
10.5593/sgem2022/1.1
1314-2704
978-619-7603-38-5
English
22
1.1
•    Prof. DSc. Oleksandr Trofymchuk, UKRAINE 
•    Prof. Dr. hab. oec. Baiba Rivza, LATVIA
Mineral Processing
ADI (Austempered Ductile Iron) - a bainitic ductile iron in which the resulting structure is obtained by the isothermal decay of austenite in the bainite region is currently a very promising material, which has a very wide application in various industries. It is characterized by a particularly favorable combination of strength and ductility, which exceeds the properties of heat-treated steels in the strength range of 800 - 1500 MPa. Its production is problematic because the ferritic or ferritic-pearlitic SGI (spheroidal graphite iron), which is a precursor in the preparation of ADI cast iron, has to meet demanding metallurgical properties, especially as many regular graphite globules evenly distributed in the matrix. The aim of this article is to present a method of metallurgical processing of SGI in such a way as to ensure the quality of the melt required for the preparation of ADI cast iron with respect to elimination of environmental impacts, i.e. inmold modification, as traditional SGI production causes exothermic reaction. work environment. Another possibility to influence the metallurgical quality of SGI cast iron is the action a magnetic field acting on the solidifying melt of SGI, which leads to improvement the metallurgical as well as mechanical properties of SGI.
[1] Keough, J.R., Hayrynen, K.L., Popovski, V.M.Continuing Developments in the Science and Application of Austempered Ductile Iron (ADI). In Proceedings of the 70th World Foundry Congress 2012, Monterrey, Mexico; Curran Associates, Inc., 2012, p. 491.
[2] Stefanescu, D.M., Ruxanda, R. Lightweight Iron Castings—Can They Replace Aluminum Castings. In Proceedings of the 65th World Foundry Congress, Gyeongju, Korea, 2002; p. 71.
[3] Gorny, M.,Stefanescu, D.M. Thin-wall ductile iron castings. In Cast Iron Science and Technology.ASM Handbook; ASM International: Columbus, OH, USA, 2017; Vol. 1A, p. 617.
[4] Pokusova, M. Effect of Moulding Sand’s Thermo-Physical Properties on the Crystallization of Ductile Cast Iron. In Scientific Proceedings Faculty of Mechanical Engineering STU in Bratislava. Bratislava: STU, 2012, pp. 22.
[5] Hlebova, S., Ambrisko, L., Pesek, L.,: Strain Measurement in Local Volume by Non-Contact Videoextensometric Technique on Ultra High Strength Steels, Key Engineering Materials, 2014, Vol. 586, pp. 129-132.
[6] Pokusova, M., Pokusa, A., Mojzis, M. Computer simulation of solidification for inmold technology. In ActaMetallurgicaSlovaca, 2007, No. 4, pp. 76.
[7] Wu, C.et al. Influence of high magnetic field annealing on structure of spheroidal graphite cast iron. In Journal of Dalian University of Technology, 2004, Iss.4, p. 514.
[8] Gumienny, G.: Carbidic bainitic and ausferritic ductile cast iron. In Archives of metallurgy and materials, 2013, No. 58, pp. 1053-1058
[9] Lu, G.X.; Zhang, H. Sliding wear characteristics of austempered ductile iron with and without laser hardening.Wear 1990, 138, 1–12
[10] Zhou, W.S.; Zhou, Q.D.; Meng, S.K. Lubricated sliding and rolling wear of austempered ductile iron. Wear, 1993, 162–164, 696–702.
[11] Fatahalla, N.; Hussein, O. Microstructure, mechanical properties, toughness, wear characteristics and fracture phenomena of austenitized and austempered low- alloyed ductile iron. Open Access Libr. J. 2015, 2, 1–16.
[12] Lin, C.K.; Hung, T.P. Influence of microstructure on the fatigue properties of austempered ductile irons—II., Low-cycle fatigue. Int. J. Fatigue 1996, 18, 309–320
[13] Lin, C.K.; Lai, P.K.; Shih, T.S. Influence of microstructure on the fatigue properties of austempered ductile irons—I. High-cycle fatigue. Int. J. Fatigue 1996, 18, 297–307
[14] Trudel, A.; Gagne, M. Effect of Composition and Heat Treatment Parameters on the Characteristics of Austempered Ductile Irons. Can. Metall. Q. 1997, 36, 289– 298.
[15] Pribulova, A., Futas, P, Pokusova, M.: Influence of charge composition on ENGJS-500-7 ductile iron properties in foundry operating conditions, Materials Science Forum, 2020, Vol. 998 MSF, pp. 42 - 47
This work was supported by the Scientific Grant Agency of The Ministry of Education of the Slovak republic No. KEGA 018TUKE-4/2022, VEGA 1/0002/22, VEGA 1/0265/21 and APVV-19-0559.
conference
https://doi.org/10.5593/sgem2022/1.1/s04.056
Download PDF
Proceedings of 22nd International Multidisciplinary Scientific GeoConference SGEM 2022
22nd International Multidisciplinary Scientific GeoConference SGEM 2022, 04 - 10 July, 2022
Proceedings Paper
STEF92 Technology
International Multidisciplinary Scientific GeoConference SGEM
SWS Scholarly Society; Acad Sci Czech Republ; Latvian Acad Sci; Polish Acad Sci; Serbian Acad Sci and Arts; Natl Acad Sci Ukraine; Natl Acad Sci Armenia; Sci Council Japan; European Acad Sci, Arts and Letters; Acad Fine Arts Zagreb Croatia; Croatian Acad Sci and Arts; Acad Sci Moldova; Montenegrin Acad Sci and Arts; Georgian Acad Sci; Acad Fine Arts and Design Bratislava; Turkish Acad Sci.
483-490
04 - 10 July, 2022
website
8443
spheroidal graphite iron (SGI), austempered ductile iron (ADI), metallurgy, modification