Adjustment of compositions and processing techniques, mainly ? firing conditions, has been a key route for ceramics performance improvement. The present research addresses sintering process of alumina ceramics with an additive in system that was studied by non-isothermal method. Experimental samples shaped as cylinders 25 ? 6 mm in size were obtained and sintered by consequtive firings in air at heating rates q1 = 1,0 and q2 = 3,0 °?/min without curing and quenched in air. Linear shrinkage (? = ??/?, hereon ? ?) a...